Nature and dynamics of photoexcited states in an electroluminescent poly(phenylene vinylene-co-fluorenylene (pnylene)-based π-conjugated polymer

Chellappan Vijila*, Markus Westerling, Harri Aarnio, Ronald Österbacka, Huang Chun, Chen Zhikuan, Zhang Xinhai, Zhu Furong, Chua Soo Jin

*Korresponderande författare för detta arbete

Forskningsoutput: TidskriftsbidragArtikelVetenskapligPeer review

6 Citeringar (Scopus)

Sammanfattning

This paper describes the optical properties of an electroluminescent poly(phenylene vinylene-cofluorenylene vinylene) (BPPPV-PF)-based π-conjugated polymer using absorption, photoluminescence (PL), time-resolved photoluminescence (TRPL), continuous wave (CW) and transient-photoinduced absorption (PA) spectroscopic techniques. The TRPL decay spectra of BPPPV-PF in chloroform and film exhibit single exponential decay with PL lifetimes of 0.8 ns and 0.2 ns, respectively. The CW-PA spectrum exhibits a singlewell-defined band centred at 1.5 eV, which is assigned to the T-T* transition of the triplet excitons. The monomolecular lifetime (b) of the triplet excitons was estimated from the intensity dependence of CW-PA and found to be ∼1.2 ms at 80 K. The temperature dependence of the CW-PA signal at 1.5 eV was studied for a temperature range from 80 K to 298 K. It was observed that the PA signal at 1.5 eV was persistent to relatively high temperatures, which may be due to the bulky side chain of the polymer and morphology of the film. The relaxation process of this triplet excitationwas studied by measuring the transient decay of the PA signal for various temperatures. The transient-PA signal shows monomolecular recombination process at all recorded temperatures and the temperature dependence of monomolecular lifetime (t) was studied. It was found that the monomolecular lifetime (τ) is dependent on temperature but independent of the laser excitation intensity. The obtained results are analyzed based on the molecular structure of the PPV-PF copolymer.

OriginalspråkEngelska
Sidor (från-till)358-362
Antal sidor5
TidskriftJournal of Photochemistry and Photobiology A: Chemistry
Volym199
Nummer2-3
DOI
StatusPublicerad - 25 sep. 2008
MoE-publikationstypA1 Tidskriftsartikel-refererad

Fingeravtryck

Fördjupa i forskningsämnen för ”Nature and dynamics of photoexcited states in an electroluminescent poly(phenylene vinylene-co-fluorenylene (pnylene)-based π-conjugated polymer”. Tillsammans bildar de ett unikt fingeravtryck.

Citera det här