Magnetoresistance effect in the fluctuating-valence BaSmFe2O5+w system

J. Nakamura; J. Lindén; M. Karppinen; H. Yamauchi

doi:10.1063/1.1310170

Magnetoresistance effect in the fluctuating-valence BaSmFe₂O_5+w system

J. Nakamura^*
, J. Lindén
, M. Karppinen
, H. Yamauchi

^*Korresponderande författare för detta arbete

Fysik

Forskningsoutput: Tidskriftsbidrag › Artikel › Vetenskaplig › Peer review

13 Citeringar (Scopus)

Sammanfattning

The occurrence of negative magnetoresistance (MR) in semiconductive BaSmFe₂O_5+w double-perovskite samples is demonstrated. A peak in the MR value was observed at the Verwey-type transition temperature. The transition signifies the charge separation of the Fe^2.5+ fluctuating mixed valence state into high-spin Fe²⁺ and Fe_3-. The samples were ferrimagnetic with a Curie temperature of ∼ 710 K. Upon oxidizing/reducing the samples the size of the MR peak and the temperature at which the peak occurred varied. The largest MR value observed was 1.4% at 7 T.

Originalspråk	Engelska
Sidor (från-till)	1683-1685
Antal sidor	3
Tidskrift	Applied Physics Letters
Volym	77
Nummer	11
DOI	https://doi.org/10.1063/1.1310170
Status	Publicerad - 11 sep. 2000
MoE-publikationstyp	A1 Tidskriftsartikel-refererad

Åtkomst av dokument

10.1063/1.1310170

Andra filer och länkar

Link to publication in Scopus

Citera det här

@article{fc996517fceb4fbf8870cb700bc07ac3,

title = "Magnetoresistance effect in the fluctuating-valence BaSmFe2O5+w system",

abstract = "The occurrence of negative magnetoresistance (MR) in semiconductive BaSmFe2O5+w double-perovskite samples is demonstrated. A peak in the MR value was observed at the Verwey-type transition temperature. The transition signifies the charge separation of the Fe2.5+ fluctuating mixed valence state into high-spin Fe2+ and Fe3-. The samples were ferrimagnetic with a Curie temperature of ∼ 710 K. Upon oxidizing/reducing the samples the size of the MR peak and the temperature at which the peak occurred varied. The largest MR value observed was 1.4\% at 7 T.",

author = "J. Nakamura and J. Lind{\'e}n and M. Karppinen and H. Yamauchi",

year = "2000",

month = sep,

day = "11",

doi = "10.1063/1.1310170",

language = "English",

volume = "77",

pages = "1683--1685",

journal = "Applied Physics Letters",

issn = "0003-6951",

publisher = "American Institute of Physics",

number = "11",

}

TY - JOUR

T1 - Magnetoresistance effect in the fluctuating-valence BaSmFe2O5+w system

AU - Nakamura, J.

AU - Lindén, J.

AU - Karppinen, M.

AU - Yamauchi, H.

PY - 2000/9/11

Y1 - 2000/9/11

N2 - The occurrence of negative magnetoresistance (MR) in semiconductive BaSmFe2O5+w double-perovskite samples is demonstrated. A peak in the MR value was observed at the Verwey-type transition temperature. The transition signifies the charge separation of the Fe2.5+ fluctuating mixed valence state into high-spin Fe2+ and Fe3-. The samples were ferrimagnetic with a Curie temperature of ∼ 710 K. Upon oxidizing/reducing the samples the size of the MR peak and the temperature at which the peak occurred varied. The largest MR value observed was 1.4% at 7 T.

AB - The occurrence of negative magnetoresistance (MR) in semiconductive BaSmFe2O5+w double-perovskite samples is demonstrated. A peak in the MR value was observed at the Verwey-type transition temperature. The transition signifies the charge separation of the Fe2.5+ fluctuating mixed valence state into high-spin Fe2+ and Fe3-. The samples were ferrimagnetic with a Curie temperature of ∼ 710 K. Upon oxidizing/reducing the samples the size of the MR peak and the temperature at which the peak occurred varied. The largest MR value observed was 1.4% at 7 T.

UR - https://www.scopus.com/pages/publications/0000012853

U2 - 10.1063/1.1310170

DO - 10.1063/1.1310170

M3 - Article

AN - SCOPUS:0000012853

SN - 0003-6951

VL - 77

SP - 1683

EP - 1685

JO - Applied Physics Letters

JF - Applied Physics Letters

IS - 11