Influence of SrO substitution for CaO on the properties of bioactive glass S53P4

Jonathan Massera, Leena Hupa

    Forskningsoutput: TidskriftsbidragArtikelVetenskapligPeer review

    42 Citeringar (Scopus)

    Sammanfattning

    Commercial melt-quenched bioactive glasses consist of the oxides of silicon, phosphorus, calcium and sodium. Doping of the glasses with oxides of some other elements is known to affect their capability to support hydroxyapatite formation and thus bone tissue healing but also to modify their high temperature processing parameters. In the present study, the influence of gradual substitution of SrO for CaO on the properties of the bioactive glass S53P4 was studied. Thermal analysis and hot stage microscopy were utilized to measure the thermal properties of the glasses. The in vitro bioactivity and solubility was measured by immersing the glasses in simulated body fluid for 6 h to 1 week. The formation of silica rich and hydroxyapatite layers was assessed from FTIR spectra analysis and SEM images of the glass surface. Increasing substitution of SrO for CaO decreased all characteristic temperatures and led to a slightly stronger glass network. The initial glass dissolution rate increased with SrO content. Hydroxyapatite layer was formed on all glasses but on the SrO containing glasses the layer was thinner and contained also strontium. The results suggest that substituting SrO for CaO in S53P4 glass retards the bioactivity. However, substitution greater than 10 mol% allow for precipitation of a strontium substituted hydroxyapatite layer.
    OriginalspråkOdefinierat/okänt
    Sidor (från-till)657–668
    TidskriftJournal of Materials Science: Materials in Medicine
    Volym25
    Utgåva3
    DOI
    StatusPublicerad - 2014
    MoE-publikationstypA1 Tidskriftsartikel-refererad

    Citera det här