Films from glyoxal-crosslinked spruce galactoglucomannans plasticized with sorbitol

Kirsi S. Mikkonen*, Mari I. Heikkilä, Stefan M. Willför, Maija Tenkanen

*Korresponderande författare för detta arbete

Forskningsoutput: TidskriftsbidragArtikelVetenskapligPeer review

38 Citeringar (Scopus)

Sammanfattning

Films were prepared from a renewable and biodegradable forest biorefinery product, spruce O-acetyl-galactoglucomannans (GGMs), crosslinked with glyoxal. For the first time, cohesive and self-standing films were obtained from GGM without the addition of polyol plasticizer. In addition, glyoxal-crosslinked films were prepared using sorbitol at 10, 20, 30, and 40% (wt.-% of GGM). Glyoxal clearly strengthened the GGM matrix, as detected by tensile testing and dynamic mechanical analysis. The elongation at break of films slightly increased, and Young's modulus decreased with increasing sorbitol content. Interestingly, the tensile strength of films was constant with the increased plasticizer content. The effect of sorbitol on water sorption and water vapor permeability (WVP) depended on relative humidity (RH). At low RH, the addition of sorbitol significantly decreased the WVP of films. The glyoxal-crosslinked GGM films containing 20% sorbitol exhibited the lowest oxygen permeability (OP) and WVP of the studied films and showed satisfactory mechanical performance.

OriginalspråkEngelska
Artikelnummer482810
TidskriftInternational Journal of Polymer Science
Volym2012
DOI
StatusPublicerad - 2012
MoE-publikationstypA1 Tidskriftsartikel-refererad

Fingeravtryck Fördjupa i forskningsämnen för ”Films from glyoxal-crosslinked spruce galactoglucomannans plasticized with sorbitol”. Tillsammans bildar de ett unikt fingeravtryck.

Citera det här