Control of Fe valence state and magnetoresistance by means of T=Ta and W substitution in Sr2Fe(Mo1-xTx)O6

J. Lindén, T. Yamamoto, J. Nakamura, H. Yamauchi, M. Karppinen*

*Korresponderande författare för detta arbete

Forskningsoutput: TidskriftsbidragArtikelVetenskapligPeer review

29 Citeringar (Scopus)

Sammanfattning

High-purity Sr2Fe(Mo1-xTx)O6 samples with T=W, Ta and 0≤×≤1 were obtained by means of encapsulation synthesis. For the nonsubstituted samples earlier 57Fe Mössbauer spectroscopy measurements indicate that the Fe ions occupy a fluctuating mixed-valence state of +2.5. [J. Lindén et al. Appl. Phys. Lett. 76 (2000) 2925.] WVI substitution causes increasing amounts of Fe to enter the II state, whereas TaV substitution yields increasing amounts of FeIII. Both substitution schemes lead to a decrease in the intensity of the component assigned to Fe2.5+. Nonsubstituted samples exhibit a characteristic tunneling-type magnetoresistance below Tc. Both W and Ta substitution were found to enhance the low-temperature magnetoresistance around the Néel temperature of the pure Sr2FeWO6 and Sr2FeTaO6 phases, respectively. The enhancement appears to be related to the colossal magnetoresistance (CMR) effect at the paramagnetic to antiferromagnetic transitions in the areas rich in W or Ta. The transition and consequently the region of non-zero CMR effect are rather broad due to the glass-like behavior of the highly-substituted samples within the low-temperature region. Ta substitution had a stronger influence on the transport properties, magnetization and mixed valency than W substitution had. It is suggested that TaV disrupts the double-exchange interaction responsible for the magnetism in the Sr2FeMoO6 more efficiently than WVI.

OriginalspråkEngelska
Artikelnummer184408
Sidor (från-till)1844081-1844087
Antal sidor7
TidskriftPhysical Review B - Condensed Matter and Materials Physics
Volym66
Utgåva18
DOI
StatusPublicerad - 1 nov 2002
MoE-publikationstypA1 Tidskriftsartikel-refererad

Fingeravtryck Fördjupa i forskningsämnen för ”Control of Fe valence state and magnetoresistance by means of T=Ta and W substitution in Sr<sub>2</sub>Fe(Mo<sub>1-x</sub>T<sub>x</sub>)O<sub>6</sub>”. Tillsammans bildar de ett unikt fingeravtryck.

Citera det här