Bioactive glass compositions suitable for repeated heat-treatments

H Arstila, D Zhang, E Vedel, Leena Hupa, H Ylanen, Mikko Hupa

    Forskningsoutput: TidskriftsbidragArtikelVetenskapligPeer review

    6 Citeringar (Scopus)

    Sammanfattning

    The crystallization tendency for 30 experimental glasses in the system Na2O-K2O-MgO-CaO-B2O3-P2O5-SiO2 was studied with thermal methods, DTA, HSM and XRD. The glasses were also immersed into simulated body fluid for 8 and 72 hours. The formation of the silica-rich gel and calcium phosphate layer on the glasses were analyzed with SEM. The in vitro behavior and crystallization tendency for heat-treated glasses were then related. This information is essential for choosing glass compositions that can be manufactured to desired products with controlled bioactivity for different applications. In general, glasses with low alkali content can tolerate heat-treatment without crystallization but have less initial Si-gel formation ability and show less in vitro bioactivity than glasses with high alkali content.
    OriginalspråkOdefinierat/okänt
    Sidor (från-till)925–928
    Antal sidor4
    TidskriftKey Engineering Materials
    Volym284-286
    UtgåvaBioceramics 17
    DOI
    StatusPublicerad - 2005
    MoE-publikationstypA1 Tidskriftsartikel-refererad

    Nyckelord

    • bioactivity
    • in vitro

    Citera det här