Annealing characteristics and calcium doping effects in the superconducting Pb2CuSr2[Eu1-xCax]Cu 2O8+δ system

T. Karlemo*, M. Karppinen, L. Niinistö, J. Lindén, M. Lippmaa

*Korresponderande författare för detta arbete

Forskningsoutput: TidskriftsbidragArtikelVetenskapligPeer review

6 Citeringar (Scopus)


Essentially single-phase samples of Pb2CuSr2[Eu1-xCax]Cu 2O8+δ have been investigated in a compositional range of x = 0.0-0.3. Annealing characteristics in oxygen and nitrogen atmospheres were systematically monitored by thermogravimetric measurements. Activation energies were determined for both the oxygen uptake and loss processes. The effect of Ca doping on the critical temperature was studied, and the Tc was found to be quite independent of the Ca content. The highest value of Tc = 74 K was measured for the sample of x = 0.25. The hyperfine parameters of the Eu site were determined by 151Eu Mössbauer spectroscopy. The asymmetry parameter η of the electric field gradient showed a clear dependence on both x and δ.

Sidor (från-till)225-232
Antal sidor8
TidskriftPhysica C: Superconductivity and its Applications
StatusPublicerad - 20 dec 1997
MoE-publikationstypA1 Tidskriftsartikel-refererad

Fingeravtryck Fördjupa i forskningsämnen för ”Annealing characteristics and calcium doping effects in the superconducting Pb<sub>2</sub>CuSr<sub>2</sub>[Eu<sub>1-x</sub>Ca<sub>x</sub>]Cu <sub>2</sub>O<sub>8+δ</sub> system”. Tillsammans bildar de ett unikt fingeravtryck.

Citera det här