Valence mixing, separation and ordering in double-cell perovskite GdBaFe2O5+w

J. Lindén*, P. Karen, H. Yamauchi, M. Karppinen

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArtikkeliTieteellinenvertaisarvioitu

1 Sitaatiot (Scopus)

Abstrakti

Thermally induced valence mixing Fe2+ + Fe3+ ↔ Fe2.5+ is studied in GdBaFe2O5+w by 57Fe Mössbauer spectroscopy. For compositions close to w = 0, a two-step Verwey-type transition is registered that separates Fe2.5+ into intermediate valence- and spin states Fe2.5-ε and Fe 2.5+ε and then into the integer valences Fe2+ and Fe3+. Both steps are accompanied by a proportional decrease in electrical conductivity, altogether by approximately two orders of magnitude, and small magnetoresistance peaks are observed. Seebeck measurements identify holes as charge carriers. Increasing oxygen nonstoichiometry eliminates rapidly the first step, whereas the generally stronger Verwey transition proper persists up to levels of w≈0.25.

AlkuperäiskieliEnglanti
Sivute267-e268
JulkaisuJournal of Magnetism and Magnetic Materials
Vuosikerta272-276
NumeroSupplement
DOI - pysyväislinkit
TilaJulkaistu - toukokuuta 2004
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Valence mixing, separation and ordering in double-cell perovskite GdBaFe<sub>2</sub>O<sub>5+w</sub>'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Viittausmuodot