Two dimensional Langevin recombination in regioregular poly(3- hexylthiophene)

Gytis Juška*, Kristijonas Genevičius, Nerijus Nekrašas, Gytis Sliaužys, Ronald Österbacka

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArtikkeliTieteellinenvertaisarvioitu

69 Sitaatiot (Scopus)

Abstrakti

In this work, it is shown that recombination in regioregular poly(3-hexylthiophene):[6,6]-phenyl-C61-butyric acid methyl ester (RRP3HT:PCBM) bulk-heterojunction solar cells is caused by the two dimensional (2D) Langevin recombination in the lamellar structures of RRP3HT, which are formed after annealing process. Due to 2D Langevin process, bimolecular recombination coefficient is reduced in comparison with three dimensional Langevin case, and bimolecular recombination coefficient depends on the density of charge carriers n1/2. Data obtained from the different experimental techniques (charge extraction with linearly increasing voltage, integral time of flight, double injection current transients and transient absorption spectroscopy) confirms 2D Langevin recombination in RR3PHT.

AlkuperäiskieliEnglanti
Artikkeli013303
JulkaisuApplied Physics Letters
Vuosikerta95
Numero1
DOI - pysyväislinkit
TilaJulkaistu - 2009
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Two dimensional Langevin recombination in regioregular poly(3- hexylthiophene)'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Viittausmuodot