The effect of flame treatment on surface properties and heat sealability of low-density polyethylene coating

Mikko Tuominen, M. Ek, Pauliina Saloranta, Martti Toivakka, J. Kuusipalo

    Tutkimustuotos: LehtiartikkeliArtikkeliTieteellinenvertaisarvioitu

    6 Sitaatiot (Scopus)

    Abstrakti

    The target of this study is to investigate the correlation between surface properties and heat sealability of flame-treated low-density polyethylene (LDPE) coating because it is vital to know how to modify the surface properties of LDPE coating without losing the heat sealing properties. Flame treatment showed a significant effect on the heat sealing properties of LDPE-coated paper. For example, the heat sealing temperature of LDPE coating decreased or alternatively doubled, depending on the equivalence ratio (air-propane ratio) of flame treatment. In addition, the hot tack strength was significantly enhanced by flame treatment, which broadened the hot tack window of LDPE-coated paper. The reason for the heat sealing performance of flame-treated LDPE coating was believed to be related to the simultaneous reactions, that is, cross-linking and chain scission, occurring on the LDPE surface. The molecular weight of LDPE surface increased or decreased, depending on the dominating reaction during flame treatment. This affected the chain mobility and the amount of chain interdiffusion across the seal interface and finally defined the heat sealing performance of LDPE-coated paper.
    AlkuperäiskieliEi tiedossa
    Sivut201–214
    Sivumäärä14
    JulkaisuPackaging Technology and Science
    Vuosikerta26
    Numero4
    DOI - pysyväislinkit
    TilaJulkaistu - 2013
    OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

    Keywords

    • equivalence ratio
    • flame treatment
    • heat sealing
    • hot tack
    • LDPE coating
    • surface characterization