Scale-up of manufacturing of printed enzyme electrodes for enzymatic power source applications

Saara Tuurala, Otto-Ville Kaukoniemi, Leo von Hertzen, Johanna Uotila, Anu Vaari, Mikael Bergelin, Pia Sjöberg-Eerola, Jan-Erik Eriksson, Maria Smolander

    Tutkimustuotos: LehtiartikkeliArtikkeliTieteellinenvertaisarvioitu

    5 Sitaatiot (Scopus)

    Abstrakti

    Production of printable enzymatic power sources was scaled up from laboratory to roll-to-roll (R2R) pilot production. The anode and cathode enzymes were glucose oxidase (GOx) and laccase, respectively. The best laboratory-scale cells had a maximum power and energy density of 1.4 +/- A 0.1 A mu W cm(-2) and 5.5 +/- A 0.2 A mu Wh cm(-2), respectively. These values are 5 and 28 times higher compared to our previously published values. The R2R-produced cells had a maximum power and energy density of 0.40 +/- A 0.03 A mu W cm(-2) and 0.6 +/- A 0.1 A mu Wh cm(-2), respectively. This is 11 % of the best laboratory manufactured cells. It is suspected that the decrease in electrochemical performance originates from the lower mediator amount and higher drying temperature than that of the laboratory produced cells. However, the trials conducted in this work showed that printed enzymatic active layers can be fabricated and dried with a rotary screen-printing machine in R2R process. Hence, fully printed GOx//laccase power sources could be produced from R2R on a large scale for printed electronics applications.
    AlkuperäiskieliEi tiedossa
    Sivut881–892
    JulkaisuJournal of Applied Electrochemistry
    Vuosikerta44
    Numero7
    DOI - pysyväislinkit
    TilaJulkaistu - 2014
    OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

    Keywords

    • Paper-based biofuel cells
    • Enzymatic power sources
    • Printing
    • Mass production
    • Biopower sources

    Viittausmuodot