Rheological characterization of cement pastes with functional filler particles

    Tutkimustuotos: LehtiartikkeliArtikkeliTieteellinenvertaisarvioitu

    7 Sitaatiot (Scopus)

    Abstrakti

    Cement pastes were studied using conventional rheological methods. The effect of different types of functional fillers on the theological properties and hydration rate of the pastes was analysed. The fillers were found to have varying chemistry and therefore surface properties. Porous titania particles raised the cohesive energy of the paste significantly already at low additions. Limestone particles raised the cohesive energy somewhat, but clearly less than titania. The zeta potential of the particles was found to somewhat affect the rheology. Reaction rates of the pastes were measured using oscillatory rheological measurement with constant amplitude and frequency. Titania particles were found to accelerate the hydration rate more than limestone particles. Of the limestone particles pure calcite increased the reaction rate more than dolomitic limestone. When the limestone particles were modified to provide C-S-H nucleation sites the cohesive energy was raised and the reaction rate was further increased. (C) 2014 Elsevier Ltd. All rights reserved.
    AlkuperäiskieliEi tiedossa
    Sivut1–7
    Sivumäärä7
    JulkaisuCement and Concrete Research
    Vuosikerta65
    DOI - pysyväislinkit
    TilaJulkaistu - 2014
    OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

    Keywords

    • CaCO3
    • Calcium-Silicate-Hydrate (C-S-H)
    • Cement Paste
    • Kinetics
    • Rheology

    Viittausmuodot