Preparation of Cu-Cr alloy powder by mechanical alloying

Qing Zhao, Zhongbao Shao, Chengjun Liu, Maofa Jiang, Li Xuetian, Ron Zevenhoven, Henrik Saxén

    Tutkimustuotos: LehtiartikkeliArtikkeliTieteellinenvertaisarvioitu

    55 Sitaatiot (Scopus)


    A study of Cu-Cr alloy powder preparation by a newly developed mechanical alloying (MA) approach was conducted using a modified mill. Results showed that the preparation temperature was much lower in the tests employing modified mill than with traditional equipment, and that no distinct differences could be found in the products prepared by the vibratory and planetary mills. Active carbon powder was found to exhibit an excellent reducing capacity for metallic oxides, while graphite powder was found inappropriate in this process. Based on the experimental results, purified Cu-Cr alloy nano-scale grain can prepared by mechanical alloying in the modified mill at 325 degrees C for 3 h with a ball-to-powder mass ratio of 15:1. A crystal agglomeration phenomenon was also found in the final alloy powder, leading to an increase in particle size.
    AlkuperäiskieliEi tiedossa
    JulkaisuJournal of Alloys and Compounds
    DOI - pysyväislinkit
    TilaJulkaistu - 2014
    OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu


    • Cu-Cr
    • Mechanical alloying
    • Milling
    • Powder