Physicochemical design of the morphology and ultrastructure of cellulose beads

Jani Trygg, Pedro Fardim, Martin Gericke, Ermei Mäkilä, Jarno Salonen

    Tutkimustuotos: LehtiartikkeliArtikkeliTieteellinenvertaisarvioitu

    43 Sitaatiot (Scopus)

    Abstrakti

    Cellulose was dissolved in NaOH-urea-water and beads were prepared by coagulation into nitric acid as well as saline solution. Morphology and ultrastructure of the beads were modified by controlling the molarity of the acid (0-10M) and temperature (5-50°C) of the coagulation media and the cellulose concentration (3-7%). The beads were characterized by optical image analysis (shape, volume, and size distribution) and weight (total porosity). Cross-sections of CO2 critical point dried beads were studied by field emission scanning electron microscopy (FE-SEM) and specific surface areas of 336-470m(2)g(-1) were determined from nitrogen adsorption isoterms. Pore size distribution was analyzed using solute exclusion technique. Our results demonstrate that the ultrastructure can be controlled by alteration of the coagulation conditions. Changes in size, shape and surface area were substential. Also generation of micro- (⩽2Å), meso-, or macropores (⩾50Å) can be favored.
    AlkuperäiskieliEi tiedossa
    Sivut291–299
    JulkaisuCarbohydrate Polymers
    Vuosikerta93
    Numero1
    DOI - pysyväislinkit
    TilaJulkaistu - 2013
    OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

    Viittausmuodot