Melting behavior in the wollastonite-feldspar-quartz system

Thomas Kronberg*, Kaj Fröberg

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliKonferenssiartikkeliTieteellinenvertaisarvioitu

2 Sitaatiot (Scopus)

Abstrakti

The melting behavior of the wollastonite-feldspar system was studied using high-temperature microscopy. The decrease in the silhouette area of a cylindrical sample as a function of the temperature showed behavior characteristic for each mixture. The melting behavior was expressed further as three characteristic measuring points: T1, the temperature at which the material started to sinter; T2, the temperature at which the sintering was finished; and T3, the temperature at which the material started to float out.

AlkuperäiskieliEnglanti
Sivut167-177
Sivumäärä11
JulkaisuCeramic Engineering and Science Proceedings
Vuosikerta22
Numero2
TilaJulkaistu - 2001
OKM-julkaisutyyppiA4 Artikkeli konferenssijulkaisuussa
TapahtumaMaterials and Equipment and Whitewares; A Collection Presented at the 102nd Annual Meeting of The American Ceramic Society - St. Louis, MO, United States
Kesto: 29 huhtikuuta 20013 toukokuuta 2001

Sormenjälki Sukella tutkimusaiheisiin 'Melting behavior in the wollastonite-feldspar-quartz system'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Viittausmuodot