Magnetic properties of spinel oxides, InFeMO4 (M=Mg, Co and Ni)

M. Matvejeff*, J. Lindén, T. Motohashi, M. Karppinen, H. Yamauchi

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArtikkeliTieteellinenvertaisarvioitu

6 Sitaatiot (Scopus)

Abstrakti

The impact of cation composition on the magnetic properties in the InFeMO4 mixed spinel system (M=Mg,Co,Ni) has been studied by means of AC/DC magnetization and 57Fe Mössbauer spectroscopy measurements. Existence of a glassy state was confirmed for InFeCoO4 by AC magnetization measurement, whereas the shape of the hysteresis loop in M - H measurement suggests the presence of strong interactions between the magnetic clusters. Soft magnet-type behaviour was observed for InFeNiO4 with the value of saturation magnetization suggesting the presence of canted spin structure as a consequence of the presence of nonmagnetic indium. In the case of InFeMgO4 the further magnetic dilution due to nonmagnetic magnesium was observed to lead to clear decay in long-range magnetic order, although the presence of short-range magnetic order was confirmed by M - H and 57Fe Mössbauer measurements.

AlkuperäiskieliEnglanti
Sivut249-254
Sivumäärä6
JulkaisuSolid State Communications
Vuosikerta144
Numero5-6
DOI - pysyväislinkit
TilaJulkaistu - marraskuuta 2007
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Magnetic properties of spinel oxides, InFeMO<sub>4</sub> (M=Mg, Co and Ni)'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Viittausmuodot