Intermixing of Fe at Cu(1)-chain and Cu(2)-plane sites in FeSr2YCu2O7.30 system: A neutron diffraction and Mössbauer spectroscopic study

V. P.S. Awana*, S. K. Malik, W. B. Yelon, J. Lindén, M. Karppinen, H. Yamauchi

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliKonferenssiartikkeliTieteellinenvertaisarvioitu

7 Sitaatiot (Scopus)

Abstrakti

The presently prepared FeSr2YCu2Oz (Fe-1212) sample crystallizes in a tetragonal structure (space group P4/mmm). Rietveld structural refinement of the room temperature neutron diffraction data reveal that nearly half of the Fe remains at the Cu(1)-chain site while the other half goes to the Cu(2)-plane site in the nominal Cu(1)Sr2YCu(2)2O7 or Cu-1212 structure. In this compound, Cu is distributed over the chain and plane sites appropriately. Oxygen content of the present Fe-1212 sample, as determined from the oxygen occupancies, is 7.30(2) per formula unit. Existence of Fe at the two different lattice sites is also confirmed from the room temperature 57Fe Mössbauer spectrum of the compound.

AlkuperäiskieliEnglanti
Sivut62-64
Sivumäärä3
JulkaisuPhysica B: Condensed Matter
Vuosikerta312-313
DOI - pysyväislinkit
TilaJulkaistu - maaliskuuta 2002
OKM-julkaisutyyppiA4 Artikkeli konferenssijulkaisuussa
TapahtumaInternational Conference on Strongly Correlated Electrons - Ann Arbor, MI, United States
Kesto: 6 elokuuta 20026 elokuuta 2002

Sormenjälki Sukella tutkimusaiheisiin 'Intermixing of Fe at Cu(1)-chain and Cu(2)-plane sites in FeSr<sub>2</sub>YCu<sub>2</sub>O<sub>7.30</sub> system: A neutron diffraction and Mössbauer spectroscopic study'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Viittausmuodot