Influence of composition on the formation of melt near the floor tubing of kraft recovery boilers

R Backman; Mikko Hupa; Berndt Södergård; M Pulliainen; C Svensson

Influence of composition on the formation of melt near the floor tubing of kraft recovery boilers

R Backman, Mikko Hupa, Berndt Södergård, M Pulliainen, C Svensson

Tutkimustuotos: Artikkeli kirjassa/raportissa/konferenssijulkaisussa › Konferenssiartikkeli › Tieteellinen › vertaisarvioitu

Abstrakti

Smelt bed samples from kraft recovery boilers were taken and chem. anal. was made at different depths in the smelt bed. Lab. measurements with synthetic salt mixts. were done as well as measurements of elec. cond. of Li2CO3 and Na2CO3 melting salt mixts. The results show that sulfur, chlorine and potassium can enrich in the lowest layer of the smelt bed. The change in compn. can lead to formation of molten phase at temps. near floor tube metal temps. Already a small amt. of melt causes the elec. cond. to increase with several orders of magnitude. Theor. calcns. support the exptl. findings.

Alkuperäiskieli	Ei tiedossa
Otsikko	10th International Symposium on Corrosion in the Pulp and Paper Industry
Toimittajat	T Hakkarainen
Kustantaja	VTT
Sivut	57–72
ISBN (painettu)	951-38-5724-7
Tila	Julkaistu - 2001
OKM-julkaisutyyppi	A4 Artikkeli konferenssijulkaisuussa
Tapahtuma	conference; 2001-08-21; 2001-08-24 - Marina Congress Center, Helsinki, Finland Kesto: 21 elok. 2001 → 24 elok. 2001

Konferenssi

Konferenssi	conference; 2001-08-21; 2001-08-24
Ajanjakso	21/08/01 → 24/08/01

Viittausmuodot

@inproceedings{ffece53c894c4191bfa4eda73e8b74ea,

title = "Influence of composition on the formation of melt near the floor tubing of kraft recovery boilers",

abstract = "Smelt bed samples from kraft recovery boilers were taken and chem. anal. was made at different depths in the smelt bed. Lab. measurements with synthetic salt mixts. were done as well as measurements of elec. cond. of Li2CO3 and Na2CO3 melting salt mixts. The results show that sulfur, chlorine and potassium can enrich in the lowest layer of the smelt bed. The change in compn. can lead to formation of molten phase at temps. near floor tube metal temps. Already a small amt. of melt causes the elec. cond. to increase with several orders of magnitude. Theor. calcns. support the exptl. findings.",

author = "R Backman and Mikko Hupa and Berndt S{\"o}derg{\aa}rd and M Pulliainen and C Svensson",

year = "2001",

language = "Odefinierat/ok{\"a}nt",

isbn = "951-38-5724-7",

pages = "57–72",

editor = "T Hakkarainen",

booktitle = "10th International Symposium on Corrosion in the Pulp and Paper Industry",

publisher = "VTT",

note = "conference; 2001-08-21; 2001-08-24 ; Conference date: 21-08-2001 Through 24-08-2001",

}

Influence of composition on the formation of melt near the floor tubing of kraft recovery boilers. / Backman, R; Hupa, Mikko; Södergård, Berndt et al.
10th International Symposium on Corrosion in the Pulp and Paper Industry. toim. / T Hakkarainen. VTT, 2001. s. 57–72.

Tutkimustuotos: Artikkeli kirjassa/raportissa/konferenssijulkaisussa › Konferenssiartikkeli › Tieteellinen › vertaisarvioitu

TY - GEN

T1 - Influence of composition on the formation of melt near the floor tubing of kraft recovery boilers

AU - Backman, R

AU - Hupa, Mikko

AU - Södergård, Berndt

AU - Pulliainen, M

AU - Svensson, C

PY - 2001

Y1 - 2001

N2 - Smelt bed samples from kraft recovery boilers were taken and chem. anal. was made at different depths in the smelt bed. Lab. measurements with synthetic salt mixts. were done as well as measurements of elec. cond. of Li2CO3 and Na2CO3 melting salt mixts. The results show that sulfur, chlorine and potassium can enrich in the lowest layer of the smelt bed. The change in compn. can lead to formation of molten phase at temps. near floor tube metal temps. Already a small amt. of melt causes the elec. cond. to increase with several orders of magnitude. Theor. calcns. support the exptl. findings.

AB - Smelt bed samples from kraft recovery boilers were taken and chem. anal. was made at different depths in the smelt bed. Lab. measurements with synthetic salt mixts. were done as well as measurements of elec. cond. of Li2CO3 and Na2CO3 melting salt mixts. The results show that sulfur, chlorine and potassium can enrich in the lowest layer of the smelt bed. The change in compn. can lead to formation of molten phase at temps. near floor tube metal temps. Already a small amt. of melt causes the elec. cond. to increase with several orders of magnitude. Theor. calcns. support the exptl. findings.

M3 - Konferensbidrag

SN - 951-38-5724-7

SP - 57

EP - 72

BT - 10th International Symposium on Corrosion in the Pulp and Paper Industry

A2 - Hakkarainen, T

PB - VTT

T2 - conference; 2001-08-21; 2001-08-24

Y2 - 21 August 2001 through 24 August 2001

ER -