Growth of 57Fe-doped YBa2Cu3O7-δ single crystals for Mössbauer and susceptibility measurements

I. Tittonen*, J. Hietaniemi, J. Huttunen, M. Karppinen, T. Katila, J. Lindén, L. Niinistö, K. Ullakko

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArtikkeliTieteellinenvertaisarvioitu

1 Sitaatiot (Scopus)

Abstrakti

57Fe-doped and undoped single crystals were grown for Mössbauer and magnetic AC susceptibility measurements. The effects of cooling rate and the concentration of the YBa2(Cu1-x57Fex)3O7-δ-powder in the melt were examined. The lattice parameters of the single crystals were determined by x-ray diffraction. Growth in air yielded orthorhombic crystals with a- and b-axes differing only slightly and having Tc=77K for undoped and 57 K for 57Fe-doped crystals. Mössbauer spectra indicated the presence of regions with different oxygen contents.

AlkuperäiskieliEnglanti
Sivut1259-1260
Sivumäärä2
JulkaisuPhysica C: Superconductivity and its Applications
Vuosikerta162-164
NumeroPart 2
DOI - pysyväislinkit
TilaJulkaistu - joulukuuta 1989
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'Growth of <sup>57</sup>Fe-doped YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> single crystals for Mössbauer and susceptibility measurements'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Viittausmuodot