Influence of the specific surface area and silver crystallite size of mesoporous Ag/SrTiO3 on the selectivity enhancement of ethylene oxide production

Shekoufeh Adhami, Mohsen Nasr Esfahany, Kari Eränen, Markus Peurla, Ermei Mäkilä, Dmitry Murzin, Tapio Salmi

Research output: Contribution to journalArticleScientificpeer-review

2 Citations (Scopus)
1 Downloads (Pure)

Abstract

BackgroundEthylene oxide, which is industrially produced by ethylene epoxidation, is an important versatile chemical intermediate, thus its selectivity enhancement can bring substantial economic profits. In this work, the effects of two important, but still debatable, factors, i.e. catalyst specific surface area and active phase crystallite size, on the catalyst selectivity enhancement were investigated. Surfactant assisted sol–gel method with good control ability on the pores structure was selected to produce mesoporous strontium titanate (SrTiO3) nanocrystals with various specific surface area. The SrTiO3 nanocrystals were used as the supports of silver (Ag) for ethylene epoxidation.ResultsThe Ag/SrTiO3 catalysts with various surface areas were obtained by changing the surfactant‐alkoxide ratio and the calcination time. The ethylene oxide selectivity of the prepared catalysts was examined in a laboratory‐scale fixed bed reactor. The best performance was observed at the lowest surfactant–alkoxide ratio of 0.2 and calcination time of 4 h, with the surface area of 1.7 m2/g and Ag crystallite size of 15 nm.ConclusionThe best catalyst selectivity was observed at the lowest surface area and the highest average Ag crystallite size. In this condition, the selectivity of the Ag/SrTiO3 catalyst without any modifier was superior to a commercial Ag/Al2O3 catalyst with 3.7m2/g surface area and alkaline earth metal modifiers.

Original languageUndefined/Unknown
Pages (from-to)3839–3849
JournalJournal of Chemical Technology and Biotechnology
Volume94
Issue number12
DOIs
Publication statusPublished - 2019
MoE publication typeA1 Journal article-refereed

Keywords

  • Chemical Reactions Engineering

Cite this