Recovery of chromium from residue of sulfuric acid leaching of chromite

A1 Originalartikel i en vetenskaplig tidskrift (referentgranskad)

Interna författare/redaktörer

Publikationens författare: Qing Zhao, Chengjun Liu, Baokuan Li, Ron Zevenhoven, Henrik Saxén, Maofa Jiang
Förläggare: Elsevier
Publiceringsår: 2018
Tidskrift: Process Safety and Environmental Protection
Tidskriftsakronym: Process Saf. Environ. Prot.
Volym: 113
Artikelns första sida, sidnummer: 78
Artikelns sista sida, sidnummer: 87
eISSN: 1744-3598


The sulfuric acid leaching process is widely considered to be a cleaner technology to prepare chromium salt from natural chromite as no Cr(VI)-bearing wastes are generated or discharged. However, some insoluble anhydrous chromium sulfate could precipitate causing a serious chromium resource loss and potential pollution problems. For the purpose of recovery of chromium from leaching residue, a Box–Behnken design (BBD) based ammonium leaching treatment is investigated and optimized. A second-order polynomial regression model that reveals the functional relationship between processing parameters and recovery time is established and verified by the analysis of variance (ANOVA). Predicted results show a good agreement with the experimental data. The main and interactive effects of the processing parameters on the recovery time are illustrated by three-dimensional (3D) response surfaces. It was found that increasing temperature (from 70 to 90 °C) and acidity (pH value from 0 to −0.5) of solution have positive effect on the leaching efficiency, and the plot of recovery time versus ammonium dosage shows a parabola-shape. On the basis of the findings in this study, an advanced sulfuric acid leaching process of chromite is proposed. Experimental results showed that hydrous and anhydrous chromium sulfate were completely recovered, and the average difference between the predicted and actual recovery times was less than 4%. All of the chromium resources can be utilized in the novel process, and no hazardous wastes or potential pollutants are discharged to the environment.


chromite, Chromium, residues, Sulfuric acid leaching