Changes in extractives and wetting properties of TMP paper during ageing

A1 Originalartikel i en vetenskaplig tidskrift (referentgranskad)


Interna författare/redaktörer


Publikationens författare: Sylwia Bialczak, Jouko Peltonen, Bjarne Holmbom, Anna Sundberg
Förläggare: AB SVENSK PAPPERSTIDNING
Publiceringsår: 2011
Tidskrift: Nordic Pulp and Paper Research Journal
Tidskriftsakronym: NORD PULP PAP RES J
Volym: 26
Nummer: 4
Artikelns första sida, sidnummer: 438
Artikelns sista sida, sidnummer: 444
Antal sidor: 7
ISSN: 0283-2631
eISSN: 2000-0669


Abstrakt

TMP-based newsprint paper was submitted to accelerated ageing at 60 degrees C for up to 7 days, natural ageing at room temperature for a year, and storage in a freezer for two years. Already after 2 days of accelerated ageing, only 20% of the original lipophilic extractives could be extracted with acetone and analysed by gas chromatography. The contact angle with water increased remarkably during accelerated ageing, already within 2 h, indicating a rapid migration of lipophilic extractives to the surface of the fibres. After this, the contact angle continued to rise slightly, and the contact angle remained high even after extraction of the paper with acetone. During this later phase the extractives are oxidised and further also polymerised, thus preventing their extraction. Similar changes were observed also in paper stored at room temperature (natural ageing), and even in paper stored in a freezer. For pre-extracted paper, the contact angle decreased, verifying that the extractives play the key role in the so-called self-sizing of paper during storage. To manage and control the surface and printing properties of paper, appropriate attention should be paid to the amount and composition of extractives and to the storage conditions, especially for paper made from mechanical pulps.


Nyckelord

Ageing of paper, Contact angle, Extractives, oxidation of extractives, Paper storage, Polymerization of extractives, Self-sizing, TMP