Conducting ink based on cellulose nanocrystals and polyaniline for flexographical printing

A1 Journal article (refereed)


Internal Authors/Editors


Publication Details

List of Authors: R.-M. Latonen, A. Määttänen, P. Ihalainen, W. Xu, M. Pesonen, M. Nurmi, C. Xu
Publisher: Royal Society of Chemistry
Publication year: 2017
Journal: Journal of Materials Chemistry C
Journal acronym: J. Mater. Chem. C
Volume number: 5
Issue number: 46
Start page: 12172
End page: 12181
eISSN: 2050-7534


Abstract

A water-based environmentally friendly electrically conducting ink composed of cellulose nanocrystals (CNC) and polyaniline (PANI) was prepared. PANI was synthesized by the emulsion polymerization approach using dodecylbenzenesulfonic acid (DBSA) as the dopant to induce spherical nanoparticulate formation. Glycerol was used to adjust the viscosity of the ink. The CNC–PANI ink was characterized by transmission electron microscopy, UV-visible spectroscopy and viscosity measurements. The ink was successfully printed on multilayer curtain coated paper by the flexographical printing method. The printed layers were characterized by optical and atomic force microscopy techniques and cyclic voltammetry. A stable nanoparticulate CNC–PANI ink with an electrical conductivity of the printed films between 30 and 60 S cm−1 was obtained which was more than an order of magnitude higher than for the corresponding film without CNC.