Simultaneous melt and vapor induced ash deposit aging mechanisms – Mathematical model and experimental observations

A1 Originalartikel i en vetenskaplig tidskrift (referentgranskad)


Interna författare/redaktörer


Publikationens författare: Jonne Niemi, Daniel Lindberg, Markus Engblom, Mikko Hupa
Publiceringsår: 2017
Tidskrift: Chemical Engineering Science
Volym: 173
Artikelns första sida, sidnummer: 196
Artikelns sista sida, sidnummer: 207
eISSN: 1873-4405


Abstrakt

A laboratory method was used to study the effects of temperature gradients on synthetic ash deposits consisting of KCl-K2SO4 or NaCl-Na2SO4. The cross-sections of the deposits were analyzed using SEM/EDX. The deposits were observed to form multilayered morphologies, with porous inner layers and dense outer layers. In addition, the outer layer composition was homogenized. The densification and chemical homogenization occurred by liquid-phase sintering and by temperature gradient induced liquid-phase migration. Alkali chlorides were observed to migrate in the gas-phase towards the colder temperatures. The phenomenon was modeled and recognized to be temperature gradient induced Fickian gas-phase concentration diffusion. The migration rate is directly proportional to the temperature gradient and increases exponentially as a function of the absolute temperature. The microstructure of the particle of origin for the gaseous species was observed to function as a crucial limiting factor for the migration rate. The results show that temperature gradients affect the morphology and chemistry of ash deposits and induce alkali chloride migration towards the steel surface.


Nyckelord

Ash sintering, diffusion, Microstructure, sintering