Sulfuric acid leaching kinetics of South African chromite

A1 Originalartikel i en vetenskaplig tidskrift (referentgranskad)


Interna författare/redaktörer


Publikationens författare: Qing Zhao, Cheng-jun Liu, Pei-yang Shi, Bo Zhang, Mao-fa Jiang, Qing-song Zhang, Ron Zevenhoven, Henrik Saxén
Förläggare: Springer
Publiceringsår: 2015
Tidskrift: International Journal of Minerals, Metallurgy and Materials
Tidskriftsakronym: INT J MIN MET MATER
Volym: 22
Nummer: 3
Artikelns första sida, sidnummer: 233
Artikelns sista sida, sidnummer: 240
eISSN: 1869-103X


Abstrakt

The sulfuric acid leaching kinetics of South African chromite was investigated. The negative influence of a solid product layer constituted of a silicon-rich phase and chromium-rich sulfate was eliminated by crushing the chromite and by selecting proper leaching conditions. The dimensionless change in specific surface area and the conversion rate of the chromite were observed to exhibit a proportional relationship. A modified shrinking particle model was developed to account for the change in reactive surface area, and the model was fitted to experimental data. The resulting model was observed to describe experimental findings very well. Kinetics analysis revealed that the leaching process is controlled by a chemical reaction under the employed experimental conditions and the activation energy of the reaction is 48 kJ·mol−1.


Nyckelord

chromite ore treatment, leaching kinetics, physical models, sulfuric acid