In vitro hydrolysis and magnesium release of poly(D,​L-​lactide-​co-​glycolide)​-​based composites containing bioresorbable glasses and magnesium hydroxide

A1 Originalartikel i en vetenskaplig tidskrift (referentgranskad)


Interna författare/redaktörer


Publikationens författare: Peter Uppstu, Charlotta Paakki, Ari Rosling
Publiceringsår: 2015
Tidskrift: Journal of Applied Polymer Science
Volym: 132
Nummer: 41
eISSN: 1097-4628


Abstrakt

Magnesium is important for both bone growth and cartilage formation. However, the postoperative intake of antibiotics such as quinolones may cause a redn. in magnesium levels in tissue. The addn. of magnesium to scaffolds may therefore be beneficial for the regeneration of osteochondral defects. In this study, porous composite scaffolds were produced by gas foaming of poly(D,L-lactide-co-glycolide) (PLGA) rods with magnesium-contg. bioresorbable glasses and magnesium hydroxide as fillers. The in vitro hydrolytical degrdn. of the composite scaffolds in Tris buffer was followed over a 10-wk period. Mg2+ was released in a controlled manner from the scaffolds with varying release profiles between the different materials. Higher glass content resulted in a reduced mass loss compared to scaffolds with lower glass content. As a result of the foaming method, the scaffolds shrank initially, without evidence that the addn. of hydrophilic fillers would decrease the initial shrinkage.


Nyckelord

biomedical applications, Porous materials, properties and characterization

Senast uppdaterad 2020-05-07 vid 04:23